Ardex DPM 1 C Damp Proof Membrane

Description ARDEX DPM 1 C is a one coat solvent free, low viscosity, two component epoxy resin, supplied in pre-gauged units of 6kg, 10kg and 25kg. After hardening, it produces a membrane which can accommodate hygrometer readings up to 98% with high inherent bond strength. It has excellent resistance to water, grease, oil, aqueous salt solution and dilute mineral and organic acids. ARDEX DPM 1 C has been specifically developed to provide either a damp proof membrane, or to suppress residual moisture in concrete slabs and cement/sand screeds which are well compacted and sound, where readings of up to 98% RH are measured. ARDEX DPM 1 C can be used as a damp proof membrane that deals with damp concrete where a structural damp proof membrane is not present or is ineffective, with the risk of ground bearing moisture. A thinner application may be used to suppress residual moisture in concrete slabs and cement/sand screeds which are well compacted and sound, where readings of up to 92% RH are measured. See table below for details. ARDEX DPM 1 C is suitable for use on Calcium Sulphate screeds up to 90% RH, subject to the criteria below. ARDEX DPM 1 C is suitable for heated concrete and cement/sand screeds. The surface temperature should not exceed 27°C in accordance with BS 8203 and BS 5325. Substrate Preparation: Prior to application the concrete or screed substrate must be hard, sound and free of dust, laitance, dirt and other barrier materials such as paint, lime coatings, plaster and adhesive residues. Any existing screeds or levelling and smoothing compounds not resistant to moisture must also be removed. Concrete curing agents, admixtures and surface hardeners, and the residues of these products can impair adhesion and must be removed. Contaminated and very smooth substrates must be prepared using appropriate, mechanised surface preparation equipment, prior to applying the recommended ARDEX products. Then completely remove any dust and fines by the use of brushing combined with effective industrial vacuum extraction equipment. The mechanical preparation is required to a suitable depth that exposes aggregate and a sound hard surface ready to receive treatment. Very uneven, roughly textured or porous surfaces will reduce the coverage of the ARDEX DPM 1 C so pre-smoothing with ARDITEX NA is recommended. Calcium Sulphate Based Screeds: For calcium sulphate screeds that are measured >75%RH by the flooring contractor, ARDEX DPM 1 C may be used if; The screed manufacturer agrees that their screed can receive an epoxy DPM. The subfloor contains an effective damp proof membrane, and that any moisture remaining is from the construction process and not from rising moisture from the ground. The screed has been down for >28 days and has a surface tensile strength of at least 1.0 N/mm2 for smoothing applications up to 6mm thick. The moisture content measured is <1.5% w/w moisture, or <90% RH. There is no underfloor heating in place. No timber flooring is to be bonded to it. In the case that these criteria are met, apply ARDEX DPM 1 C at minimum 350 microns to the prepared substrate. Smooth with 3mm-6mm ARDITEX NA, which must be applied within 48 hours of the application of the ARDEX DPM 1 C. Movement Joints: Any joints or cracks in the floor subject to movement, such as structural movement joints, must not be bridged with the ARDEX DPM 1C. These joints must be treated with a flexible impervious jointing system and be carried through to the floor finish before a damp proof membrane is applied. Where non-moving cracks are present in the screed these should be fully stitched and filled with an appropriate resin system before a damp proof membrane is applied. Consult the ARDEX P10 SR datasheet for further information. Applications Over Underfloor Heating: The cementitious levelling screed should have been laid in accordance with BS 8204 Part 1. The underfloor heating system should have been commissioned in accordance with the manufacturer’s instruction manual and in accordance with BS 8204 Part 1. Once thermally cycled and commissioned the underfloor heating system should be turned off for 48 hours prior to, and 48 hours after, the installation of the ARDEX DPM 1 C, smoothing compound and final floor covering. The underfloor heating system should then be gradually re-commissioned to avoid rapid thermal shock and temperature variation. Mixing: In their original containers the resin and hardening agents are pre-gauged to the correct mixing ratio. The hardening agent (Component B) is added to the resin (Component A) and thoroughly mixed together with a spiral mixing paddle in a slow speed drill until a uniform colour and consistency is achieved. It is important that all the resin components have been mixed thoroughly. In order to reduce unmixed residues, pour a proportion of the mixed material into the Component B container. Mix for 30 seconds then reintroduce this material back into the main mix in the Component A container and continue to mix. ARDEX DPM 1C is ready for immediate use and has a working time of 20 minutes at 20°C. This is reduced at higher temperatures and extended at lower temperatures. At higher temperatures it is recommended that ARDEX DPM 1 C is spread out immediately after mixing, as the reaction is exothermic and the heat generated in the container will reduce the working time. Apply at temperatures above 10°C. NOTE: Back mixing ensures that no unreacted material is present and that the packaging can be safely disposed of as non-hazardous waste. Application: Apply an even coat of the mixed ARDEX DPM 1 C with a suitable V shaped notched trowel over the appropriate area, see table below. Whilst the ARDEX DPM 1 C is still wet, the serration ridges should be flattened out with a long handled short pile paint roller, initially pre-wetted with the mixed ARDEX DPM 1 C. Evenly spread the mixed unit over one of the following approximate areas, dependent on the surface texture and thickness required: Max RH (%) Min Film Thickness 6kg Coverage (m²) 10kg Coverage (m²) 25kg Coverage (m²) 85 250 microns 15 25 62.5 92 300 microns 12.6 21 52.5 98 350 microns 10.8 18 45 The applied film thickness can be checked with wet film thickness gauge. It is essential that the applied ARDEX DPM 1 C is a continuous film and free from pinholes, cavities or thin patches, which can occur on porous screeds for example, in this case an additional application, may be necessary. Smoothing And Levelling: When wood flooring is to be adhered, first prime the cured ARDEX DPM 1 C with ARDEX R 3 E Epoxy Primer, blind the surface with ARDEX Fine Aggregate and allow to cure. Vacuum off the excess fine aggregate to leave a ‘sandpaper’ finish. Apply the relevant latex or water based smoothing compound in accordance with the relevant data sheets. Latex based smoothing compounds: ARDITEX NA (min. 3mm, max. 6mm) – apply to tack dry ARDEX DPM 1 C (typically after a minimum of 6 hours at 20°C) and within 48 hours of the cured coat of ARDEX DPM 1 C. If the timescale exceeds 48 hours then prime with ARDEX P82 (maximum time limit). ARDITEX CL (min. 3mm, max. 6mm) – the surface of the ARDEX DPM 1 C must be primed with either ARDEX P4 from 6-36 hours or ARDEX P 82 from 36 hours onwards. Water based levelling & smoothing compounds (ARDEX K15, ARDEX K40): Prime the cured ARDEX DPM 1 C with ARDEX P 82. Alternatively ARDEX P 4 primer may be used if the damp proof membrane is than less than 36 hours old. Apply the primer in accordance with the relevant datasheet, and allow to dry. Apply the required ARDEX levelling compound to a minimum of 3mm, maximum 6mm and allow to dry. ARDEX K80/SD-T B Base Mix or thicker applications of underlayments (>6mm thick): Prime the cured ARDEX DPM 1 C with ARDEX R3E Epoxy Primer, fully blind the surface with ARDEX FINE AGGREGATE and allow to cure. Vacuum off the excess fine aggregate to leave a ‘sandpaper’ finish. Apply ARDEX K 80/SD-T B Base Mix in accordance with the relevant data sheets. Note: If applying any ARDEX Smoothing Compound greater than 6mm, you must prime with ARDEX R 3 E fully sand blinded with ARDEX Fine Aggregate. Note: Minimum overcoat times are indicative only and will be effected by the ambient conditions. Ensure that the surface of the ARDEX DPM is hard and dry before walking on or applying a primer or smoothing compound. Technical Data: Density at 20°C: 1.54 Working Time: 20 minutes at 20°C Over Coating if required: 6-8 hours at 20°C Walkability at 20°C: after 6 hours Colour: Black Product Datasheet Click here to view this product on the manufacturers website.